This is our main 780g woven filter cloth product.And all of our products can be customized if you need.
Our fiberglass filter cloth is widely used because of its high covering capacity , good air permeability and high filtration efficiency. Woven fiberglass is great fabric for RABH filter bag, heat-resistance.
What’s more, Our factory is equipped with 10 sets of Dornier rapier looms and 58 sets of Toyota air-jet looms to ensure stable capacity and quality. The capacity is 30,000㎡glass cloth per day.
The management team with a configuration of imported well-proven weaving equipment facilitates weaving varieties of textured fiberglass cloth up to advanced level of international quality.
Description
ES-FB780W-AR-TFM
Technical Specification Sheet
| Product Name | Acid resistant Fiberglass woven cloth 780 gsm with PTFE membrane | |
| Product Code | ES-FB780W-AR-TFM | |
| Physical properties | ||
| Weave method | Double Twill | |
| Thickness | 0.75±0.08 | |
| Weight | g/m² | 780±10 |
| Width | m | ≤2.20M |
| Loss on Ignition (%) | ≥10 | |
| Chemical Finish | Acid resistant , PTFE membrane finish | |
| Air Permeability (L/m².S@200Pa) | 50±15 | |
| Density (ROOT/INCH) | Warp | 46±2 |
| Weft | 39±2 | |
| Tensile Strength (N/25mm) | Warp | ≥2300 |
| Weft | ≥2100 | |
| Temperature | ||
| Continues temperature | C° | 260 |
| Instant temperature | C° | 280 |
The above mentioned data have been determined according to the averages obtained from a series of typical results by our lab and are intended just for reference. The technical information is subject to changes, usual tolerances apply.
Applications details
| Cement Plant | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） | Tensile Strength（N/25mm） | Running Temperature （°C） | |
| Warp | Weft | ||||||
| PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Acid-Resistant Finished + Membrane | 1/3 Twill | 340±15 | 2—5 | >10 | >1300 | >800 | ≦260 |
| Steel Plant | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） | Tensile Strength（N/25mm） | Running Temperature （°C） | |
| Warp | Weft | ||||||
| PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Acid-Resistant Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Acid-Resistant Finished + Membrane | 1/3 Twill | 340±15 | 2—5 | >10 | >1300 | >800 | ≦260 |
| Graphite Finished + Membrane | 2/5 Satin | 550±15 | 2—5 | >3 | >2000 | >2000 | ≦260 |
| Graphite Finished + Membrane | 2/5 Satin | 550±15 | 30—50 | >1.5 | >2000 | >2000 | ≦260 |
| Coal-fired Boiler | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） | Tensile Strength （N/25mm） | Running Temperature （°C） | |
| Warp | Weft | ||||||
| Acid-Resistant Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Ferroalloys | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） | Tensile Strength（N/25mm） | Running Temperature （°C） | |
| Warp | Weft | ||||||
| Acid-Resistant Finished + Membrane | 1/3 Twill | 500±15 | 2—5 | >10 | >2000 | >1200 | ≦260 |
| Acid-Resistant Finished + Membrane | 1/3 Twill | 340±15 | 2—5 | >10 | >1300 | >800 | ≦260 |
| Graphite Finished + Membrane | 2/5 Satin | 550±15 | 2—5 | >3 | >2000 | >2000 | ≦260 |
| Graphite Finished + Membrane | 2/5 Satin | 550±15 | 30—50 | >1.5 | >2000 | >2000 | ≦260 |
| Biomass Power Generation | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） | Tensile Strength（N/25mm） | Running Temperature （°C） | |
| Warp | Weft | ||||||
| PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Acid-Resistant Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Chemical Plants | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） | Tensile Strength （N/25mm） | Running Temperature （°C） | |
| Warp | Weft | ||||||
| PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Carbon Black | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） | Tensile Strength（N/25mm） | Running Temperature （°C） | |
| Warp | Weft | ||||||
| PTFE Graphite Silicone Finished | 1/3 Twill | 470±15 | 15—30 | >3 | >2000 | >1000 | ≦260 |
| Acid-Resistant Finished + Membrane | 1/3 Twill | 500±15 | 2—5 | >10 | >2000 | >1200 | ≦260 |