ES-FB360W-PSG
Technical Specification Sheet
| Product Name | Fiberglass woven cloth
360 gsm with PTFE membrane |
|
| Product Code | ES-FB360W-PSG | |
| Physical properties | ||
| Weave method | 1/3 Twill | |
| Thickness | 0.35±0.08 | |
| Weight | g/m² | 360±10 |
| Width | m | ≤2.20M |
| Loss on Ignition (%) | ≥10 | |
| Chemical Finish | Teflon , Silicon, Graphite finish | |
| Air Permeability (L/m²S@200Pa) | 380±15 | |
| Density (ROOT/INCH) |
Warp | 54±2 |
| Weft | 27±2 | |
| Tensile Strength (N/25mm) |
Warp | ≥1200 |
| Weft | ≥900 | |
| Temperature | ||
| Continues temperature | C° | 260 |
| Instant temperature | C° | 280 |
ES-FB360W-PSGM
Technical Specification Sheet
| Product Name | Fiberglass woven cloth
360 gsm with PTFE membrane |
|
| Product Code | ES-FB360W-PSGM | |
| Physical properties | ||
| Weave method | 1/3 Twill | |
| Thickness | 0.35±0.08 | |
| Weight | g/m² | 360±10 |
| Width | m | ≤2.20M |
| Loss on Ignition (%) | ≥10 | |
| Chemical Finish | Teflon , Silicon, Graphite finish, PTFE Lamination | |
| Air Permeability (L/m²S@200Pa) | 80±15 | |
| Density (ROOT/INCH) |
Warp | 54±2 |
| Weft | 27±2 | |
| Tensile Strength (N/25mm) |
Warp | ≥1200 |
| Weft | ≥900 | |
| Temperature | ||
| Continues temperature | C° | 260 |
| Instant temperature | C° | 280 |
ES-FB360W-TFI
Technical Specification Sheet
| Product Name | Fiberglass woven cloth
360 gsm with PTFE membrane |
|
| Product Code | ES-FB360W-TFI | |
| Physical properties | ||
| Weave method | 1/3 Twill | |
| Thickness | 0.35±0.08 | |
| Weight | g/m² | 360±10 |
| Width | m | ≤2.20M |
| Loss on Ignition (%) | ≥10 | |
| Chemical Finish | Teflon finish | |
| Air Permeability (L/m²S@200Pa) | 380±15 | |
| Density (ROOT/INCH) |
Warp | 54±2 |
| Weft | 27±2 | |
| Tensile Strength (N/25mm) |
Warp | ≥1200 |
| Weft | ≥900 | |
| Temperature | ||
| Continues temperature | C° | 260 |
| Instant temperature | C° | 280 |
ES-FB360W-TFM
Technical Specification Sheet
| Product Name | Fiberglass woven cloth
360 gsm with PTFE membrane |
|
| Product Code | ES-FB360W-TFM | |
| Physical properties | ||
| Weave method | 1/3 Twill | |
| Thickness | 0.35±0.08 | |
| Weight | g/m² | 360±10 |
| Width | m | ≤2.20M |
| Loss on Ignition (%) | ≥10 | |
| Chemical Finish | Teflon, PTFE Lamination | |
| Air Permeability (L/m²S@200Pa) | 80±15 | |
| Density (ROOT/INCH) |
Warp | 54±2 |
| Weft | 27±2 | |
| Tensile Strength (N/25mm) |
Warp | ≥1200 |
| Weft | ≥900 | |
| Temperature | ||
| Continues temperature | C° | 260 |
| Instant temperature | C° | 280 |
The above mentioned data have been determined according to the averages obtained from a series of typical results by our lab and are intended just for reference. The technical information is subject to changes, usual tolerances apply.
Applications details
| Cement Plant | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） |
Tensile Strength（N/25mm） | Running Temperature （°C） |
|
| Warp | Weft | ||||||
| PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Acid-Resistant Finished + Membrane | 1/3 Twill | 340±15 | 2—5 | >10 | >1300 | >800 | ≦260 |
| Steel Plant | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） |
Tensile Strength（N/25mm） | Running Temperature （°C） |
|
| Warp | Weft | ||||||
| PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Acid-Resistant Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Acid-Resistant Finished + Membrane | 1/3 Twill | 340±15 | 2—5 | >10 | >1300 | >800 | ≦260 |
| Graphite Finished + Membrane | 2/5 Satin | 550±15 | 2—5 | >3 | >2000 | >2000 | ≦260 |
| Graphite Finished + Membrane | 2/5 Satin | 550±15 | 30—50 | >1.5 | >2000 | >2000 | ≦260 |
| Coal-fired Boiler | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） |
Tensile Strength （N/25mm） |
Running Temperature （°C） |
|
| Warp | Weft | ||||||
| Acid-Resistant Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Ferroalloys | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） |
Tensile Strength（N/25mm） | Running Temperature （°C） |
|
| Warp | Weft | ||||||
| Acid-Resistant Finished + Membrane | 1/3 Twill | 500±15 | 2—5 | >10 | >2000 | >1200 | ≦260 |
| Acid-Resistant Finished + Membrane | 1/3 Twill | 340±15 | 2—5 | >10 | >1300 | >800 | ≦260 |
| Graphite Finished + Membrane | 2/5 Satin | 550±15 | 2—5 | >3 | >2000 | >2000 | ≦260 |
| Graphite Finished + Membrane | 2/5 Satin | 550±15 | 30—50 | >1.5 | >2000 | >2000 | ≦260 |
| Biomass Power Generation | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） |
Tensile Strength（N/25mm） | Running Temperature （°C） |
|
| Warp | Weft | ||||||
| PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Acid-Resistant Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Chemical Plants | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） |
Tensile Strength （N/25mm） |
Running Temperature （°C） |
|
| Warp | Weft | ||||||
| PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
| Carbon Black | |||||||
| Product Specification sheets | |||||||
| Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition （%） |
Tensile Strength（N/25mm） | Running Temperature （°C） |
|
| Warp | Weft | ||||||
| PTFE Graphite Silicone Finished | 1/3 Twill | 470±15 | 15—30 | >3 | >2000 | >1000 | ≦260 |
| Acid-Resistant Finished + Membrane | 1/3 Twill | 500±15 | 2—5 | >10 | >2000 | >1200 | ≦260 |